TOTAL Polypropylene PPC 3660
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fADVMi_TOTAL-Polypropylene-PPC-3660.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Total Petrochemicals PPC 3660 is a heterophasic copolymer polypropylene with a Melt Flow Index of 1.3 g/min for the cast extrusion of films with superior mechanical properties and retort-able. Polypropylene PPC 3660 is characterized by a low fluidity hence good melt strength to provide ease of processing and good manufactured article properties. Polypropylene PPC 3660 is intended for applications like food packaging, lamination films, stand up pouches, heat-sterilized packaging, Polypropylene PPC 3660 is suitable particularly for the extrusion of corrugated cardboard, profiles and for extrusion-thermoforming applications where high impact resistance is required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.3 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 77 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, Cast Film | 20.0 | MPa | |
| TD : Yield, 50 µm, Cast Film | 18.0 | MPa | |
| MD : Break, 50 µm, Cast Film | 60.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 34.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 500 | % | |
| TD : Break, 50 µm, Cast Film | 600 | % | |
| Dart Drop Impact (50 µm, Cast Film) | 580 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 11.0 | kN/m | |
| TD : 50.0 µm | 235.0 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | > 50 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | > 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 147 | °C | ISO 306/A50 |
| -- | 70.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 15 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 65 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFILL H 15 S 20 MJ | RIALTI Srl | PP Homopolymer | RIALFILL |
| Santoprene™ 8211-55 | ExxonMobil Chemical | TPV | Santoprene™ |
| apilon 52bio® DB 40 | API SpA | TPU-Polyester | apilon 52bio® |
| Karina BLUE PVC COMPOUND 902-06/595-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ESTOPLAST XU 6215BB51 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |