AVALON® 60 ABX
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | AVALON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f8gCWY_AVALON-60-ABX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AVALON 60 ABX is a high performance polyester based thermoplastic polyurethane for injection moulding. AVALON 60 ABX is part of the AVALON Perform Range and offers a specially designed, flexible material with improved slip resistance and rubber-like properties, particularly suitable for TPU/PU applications. The features offered include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | DIN 53479 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 60 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance | mm³ | DIN 53516 | |
| Bending life | > 1.0E+5 | Cycles | DIN 53522 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | > 15.0 | MPa | DIN 53504 |
| Tensile Elongation (Break) | > 600 | % | DIN 53504 |
| Tear Strength 1 | > 20 | kN/m | DIN 53515 |
| Additional Information |
|---|
| Test plates conditioned 20 hours at 100°C before testing |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 - 90.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 | hr | |
| Hopper Temperature | 25.0 - 35.0 | °C | |
| Rear Temperature | 150 - 170 | °C | |
| Middle Temperature | 155 - 175 | °C | |
| Front Temperature | 155 - 180 | °C | |
| Nozzle Temperature | 150 - 175 | °C | |
| Mold Temperature | 25.0 - 50.0 | °C | |
| Injection Pressure | 2.00 - 10.0 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 1.00 - 5.00 | MPa | |
| Back Pressure | 0.0300 - 0.300 | MPa | |
| Screw Speed | 20 - 80 | rpm | |
| Screw L/D Ratio | 20.0:1.0 to 25.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Typical Screw Diameter : 40 - 120 mm3 Stage Design Feed Zone : 0.4L Compression Zone : 0.3L Metering Zone : 0.3L |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 324CE | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Celstran® PA6-GF50-03 | Celanese Corporation | Nylon 6 | Celstran® |
| Hostacom EKC353N | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| Kynar® 5301 | Arkema | Plastics Additive, Other | Kynar® |
| POLYfill PPH GF5020 PD2 VT2 | Polykemi AB | PP Homopolymer | POLYfill |