CYCOLOY™ CX7240 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f8Ko9B_CYCOLOYCX7240resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLOY CX7240 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0 at 0.75mm, V1 at 0.6mm, V2 at 0.4mm and 5VB at 1.5mm respectively. Excellent flow and impact balance together with the thin wall flame resistance and all color options make CYCOLOY CX7240 an ideal candidate for a wide variety of thin wall applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2600 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 65.0 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 58.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.1 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture 5 | 100 | % | ASTM D638 |
| Fracture | 90 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2500 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 96.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 104 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 9 | 10 | kJ/m² | ISO 179/1eA |
| 23°C 10 | 22 | kJ/m² | ISO 179/1eA |
| 23°C 11 | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 180 | J/m | ASTM D256 |
| 23°C | 700 | J/m | ASTM D256 |
| -30°C 12 | 10 | kJ/m² | ISO 180/1A |
| 23°C 13 | 20 | kJ/m² | ISO 180/1A |
| 23°C 14 | 25 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 65.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 100 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 89.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 99.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 15 | 93.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 110 | °C | ASTM D1525, ISO 306/B50 13 16 |
| -- | 113 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 7.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 35 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 25 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 17 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.600 mm | V-1 | UL 94 | |
| 0.750 mm | V-0 | UL 94 | |
| 1.50 mm | 5VB | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm 17 | 960 | °C | IEC 60695-2-12 |
| 0.750 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm 18 | 775 | °C | IEC 60695-2-13 |
| 1.00 mm | 825 | °C | IEC 60695-2-13 |
| 1.50 mm 19 | 775 | °C | IEC 60695-2-13 |
| 3.00 mm | 800 | °C | IEC 60695-2-13 |
| 3.00 mm 20 | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 35 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 230 - 280 | °C | |
| Middle Temperature | 240 - 290 | °C | |
| Front Temperature | 250 - 300 | °C | |
| Nozzle Temperature | 250 - 300 | °C | |
| Processing (Melt) Temp | 250 - 300 | °C | |
| Mold Temperature | 60.0 - 85.0 | °C | |
| Vent Depth | 0.030 - 0.075 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*3 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 mm |
| 16 . | 标准 B (120°C/h), 载荷2 (50N) |
| 17 . | by VDE |
| 18 . | by VDE |
| 19 . | by VDE |
| 20 . | by VDE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chiao Fu PA66/6 MB312GM33 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66/6 | Chiao Fu PA66/6 |
| Ferro PP NPP00GT01NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| HiFill® PA11 GB30 HS | Techmer Engineered Solutions | Nylon 11 | HiFill® |
| LNP™ THERMOCOMP™ 2Z004 compound | SABIC Innovative Plastics | ETFE | LNP™ THERMOCOMP™ |
| Polyrocks 8200FP90V | Polyrocks Chemical Co., Ltd | PPE | Polyrocks |