Eastman™ GSP01
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Eastman™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f7xKO3_Eastman-GSP01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GSP01 is a clear, amorphous material. Because of its clarity, toughness and good melt strength at processing temperatures, it is useful in a variety of processing techniques including film and sheet extrusion. GSP01 may be colored using color concentrates, dry colors or liquid colorants. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 250 | µm | |
| Secant Modulus | ASTM D882 | ||
| MD : 250 µm | 1900 | MPa | |
| TD : 250 µm | 1900 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 250 µm | 52.0 | MPa | |
| TD : Yield, 250 µm | 52.0 | MPa | |
| MD : Break, 250 µm | 59.0 | MPa | |
| TD : Break, 250 µm | 55.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 250 µm | 4.0 | % | |
| TD : Yield, 250 µm | 4.0 | % | |
| MD : Break, 250 µm | 400 | % | |
| TD : Break, 250 µm | 400 | % | |
| Dart Drop Impact 1 | ASTM D1709A | ||
| -18°C, 250 µm | 500 | g | |
| 23°C, 250 µm | 400 | g | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 250 µm | 1400 | g | |
| TD : 250 µm | 1700 | g | |
| Oxygen Permeability (23°C, 250 µm, 50% RH) | 10 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 100% RH, 250 µm) | 7.0 | g/m²/24 hr | ASTM F372 |
| Carbon Dioxide Permeability 2(23°C, 250.0 µm) | 49 | cm³·mm/m²/atm/24 hr | ASTM D1434 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 37 | J/m | |
| 23°C | 100 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 70.0 | °C | |
| 1.8 MPa, Unannealed | 64.0 | °C | |
| Glass Transition Temperature | 80.0 | °C | DSC |
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 |
| CLTE - Flow (-30 to 40°C) | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity (23°C) | 0.21 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 3(23°C) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 23°C, 1 kHz | 2.60 | ||
| 23°C, 1 MHz | 2.40 | ||
| Dissipation Factor | ASTM D150 | ||
| 23°C, 1 kHz | 5.0E-3 | ||
| 23°C, 1 MHz | 0.020 | ||
| Arc Resistance | 158 | sec | ASTM D495 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 250 µm) | 108 | ASTM D2457 | |
| Transmittance | ASTM D1003 | ||
| Regular, 250 µm | 89.0 | % | |
| Total, 250 µm | 91.0 | % | |
| Clarity (250 µm) | 85.0 | ASTM D1746 | |
| Haze (250 µm) | 0.80 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 2 . | 50% RH |
| 3 . | 500 V/sec, Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Huafon JF-W-3045 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| InnoPlus LL7410D2 | PTT Global Chemical Public Company Limited | LLDPE | InnoPlus |
| Lotader® 5500 | Arkema | EEA | Lotader® |
| Moplen RP398U | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Sylvin 6238-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |