Maxxam™ PP5120R B2 SO1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f7k12Q_Maxxam-PP5120R-B2-SO1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2 |
| Tensile Stress 1(Yield) | 27.0 | MPa | ISO 527 |
| Flexural Modulus 2 | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 1.2 | kJ/m² | |
| 23°C | 2.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 63.0 | °C | ISO 75-2/A |
| Note Message | |
|---|---|
| 1 . | 5 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melos™ FM 1755 | Melos GmbH | EPM | Melos™ |
| SUMILITE® PL-1256 (Machining) | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| Geon™ BIO RA9000 | PolyOne Corporation | PVC, Flexible | Geon™ BIO |
| Hifax TRC 103P R1K3 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| LNP™ LUBRICOMP™ JZL012 compound | SABIC Innovative Plastics Europe | PESU | LNP™ LUBRICOMP™ |