LNP™ THERMOTUF™ VF006U compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f6pYeb_LNP-THERMOTUF-VF006U-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOTUF* VF006U is a compound based on Super Tough Nylon containing 30% Glass Fiber. Added features of this material are: UV Stabilized, High Impact. Also known as: LNP* THERMOTUF* Compound VF-1006 UV Product reorder name: VF006U |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.60 | % | |
| Across Flow : 24 hr | 0.90 to 2.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.50 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.72 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7790 | MPa | ASTM D638 |
| -- | 7660 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 95.0 | MPa | ASTM D638 |
| Break | 95.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.2 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 6140 | MPa | ASTM D790 |
| -- 5 | 6740 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 131 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 119 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 83 | J/m | ASTM D256 |
| 23°C 8 | 9.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 530 | J/m | ASTM D4812 |
| 23°C 9 | 34 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 17.6 | J | ASTM D3763 |
| -- | 3.60 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 253 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 254 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 235 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 237 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 277 to 288 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 293 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Europrene® HS 630 | Versalis S.p.A. | SBR, Emulsion | Europrene® |
| LEXAN™ HP3REU resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Petrothene® GA502 | LyondellBasell Industries | LLDPE | Petrothene® |
| Plaslube® POM HO CF20 TL20 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |
| Sylvin 83015-80FUV White 1576 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |