ASTALAC™ ABS M170
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f6EDnA_ASTALAC-ABS-M170.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS M170 is a high impact strength ABS designed for sheet extrusion applications requiring superior toughness and abuse resistance whilst maintaining a balance of high gloss, easy formability and product rigidity. Typical thermoformed applications include taxi driver shields, advertising signage blanks and automotive extruded bodyside strips Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS M170UV ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 14 | g/10 min | |
| 230°C/3.8 kg | 3.0 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2250 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 68.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 330 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 25.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 77.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 83.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 88.0 | °C | |
| Vicat Softening Temperature | 101 | °C | ASTM D1525 5 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Back Pressure | 10.0 to 25.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 to 190 | °C | |
| Cylinder Zone 2 Temp. | 175 to 200 | °C | |
| Cylinder Zone 3 Temp. | 180 to 205 | °C | |
| Cylinder Zone 4 Temp. | 185 to 210 | °C | |
| Cylinder Zone 5 Temp. | 190 to 220 | °C | |
| Die Temperature | 180 to 220 | °C | |
| Take-Off Roll | 75.0 to 105 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DINALON® A1X25 G33MI H | Grupo Repol | Nylon 66 | DINALON® |
| ICORENE® 1761 V2 Black 9004 | ICO Polymers EMEA, A Division of A. Schulman | mMDPE | ICORENE® |
| Lifolit® E 60.1451/1 Glow i. t. Dark 6024 | Müller Kunststoffe GmbH | PVC, Flexible | Lifolit® |
| LNP™ LUBRILOY™ RF203XXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |
| Pearlthane® 11T65D | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |