MAJORIS G374

Category:	PP, Unspecified , Polypropylene
Manufacturer:	AD majoris
Trademark:	MAJORIS
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	f5r1MQ_MAJORIS-G374.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

MAJORIS G374 is a special long glass fibre reinforced polypropylene grade, for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing with outstanding mechanical properties.

MAJORIS G374 is intended for application at low-odour and low-emission (VOC).

APPLICATIONS
MAJORIS G374 is intended for injection moulding of highly demanding technical applications.
The excellent properties of MAJORIS G374 make it suitable for:

Electrical components, automotive parts with low-odour and low-emission materials targeted at the automotive industry, interior, exterior and under the bonnet, structural furniture parts, load bearing, demanding components for various engineering sectors.

MAJORIS G374 can, in many of these applications, substitute other engineering plastics or metal alloys.

General Information
Filler / Reinforcement	Long glass fiber
Additive	heat stabilizer
Features	Low VOC Chemical coupling Recyclable materials Heat resistance, high The smell is low to none Thermal Stability
Uses	Electrical components Furniture Metal substitution Parts under the hood of a car Car interior parts Automotive exterior parts
Forms	Particle
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.12	g/cm³	ISO 1183
Molding Shrinkage	0.50	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	6400	MPa	ISO 527-2/1
Tensile Stress (Break)	112	MPa	ISO 527-2/50
Tensile Strain (Break)	3.2	%	ISO 527-2/50
Flexural Modulus ¹	5600	MPa	ISO 178
Flexural Stress ²	164	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	22	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	68	kJ/m²	ISO 179/1eU

Injection	Nominal Value	Unit
Rear Temperature	230 - 250	°C
Processing (Melt) Temp	250 - 280	°C
Mold Temperature	80.0 - 100	°C
Injection Pressure	30.0 - 60.0	MPa
Injection Rate	Slow
Screw Speed	30 - 150	rpm

Injection instructions
Holding pressure: 50 to 70% of the injection pressureBack pressure: as low as possible, 0 to 10%Holding time: as long as practical

Note Message
1 .	2.0 mm/min
2 .	2.0 mm/min

Resin Grade	Manufacturer	Category	Trademark
SCHULAMID® 6 GF 30 HI K1871	A. Schulman Europe	Nylon 6	SCHULAMID®
SUMILITE® PL-1200(1.5mm)	Sumitomo Bakelite Co., Ltd.	Phenolic	SUMILITE®
Sylvin 9468-65 Black	Sylvin Technologies Incorporated	PVC+NBR	Sylvin
Jampilen EP332L	Jam Polypropylene Company	PP Copolymer	Jampilen
Sylvin 9067-80 Grey 9469	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin