Innothane® IE-60AC
| Category: | TSU-Ester , Polyurethane Thermoset Elastomer, Polyester Based |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f5ScR3_Innothane-IE-60AC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| lE-6OAC is a tough, abrasion resistant polyester based urethane formulated for hand-batch processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.21 | g/cm³ | |
| Hardener | 1.23 | g/cm³ | |
| Base Resin | 1.27 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 50 Mix Ratio by Volume: 49 | ||
| Demold Time | 120 to 480 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.20 | Pa·s | |
| 25°C 2 | 0.58 | Pa·s | |
| 25°C 3 | 1.2 | Pa·s | |
| Curing Time (25°C) | 24 | hr | |
| Gel Time | 9.0 to 15 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 55 to 65 | ASTM D2240 | |
| Tensile Strength | 3.45 | MPa | ASTM D638 |
| Tensile Elongation at Break | 200 | % | ASTM D638 |
| Tear Strength | 13.1 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8260-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Kuraray Poval® PVA 226 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| LUVOCOM® 19-8365 | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| POLYCASA® ACRYL KR 2010/1 | Polycasa | Acrylic (PMMA) | POLYCASA® ACRYL |
| PERLER® B39V4000A01 | A.D. Compound S.p.A. | PP Homopolymer | PERLER® |