SCHULAMID® 66 MW 30 FR 4
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f4nAkQ_SCHULAMID-66-MW-30-FR-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% mineral filled flame retardant Polyamide 66 grade; without PBDE; low warpage |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.60 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 4600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 100 | 55.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.8 | 9.0 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 2.8 | -- | kJ/m² | |
| 23°C | 3.0 | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | -- | kJ/m² | |
| 23°C | 35 | 58 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 202 | -- | °C | ISO 75-2/Af |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 300 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 100 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | V-0 | -- | ||
| 0.750 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 750 | -- | °C | |
| 1.50 mm | 750 | -- | °C | |
| 3.00 mm | 750 | -- | °C | |
| Oxygen Index | 33 | -- | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2285 HF TFE 15 | RTP Company | PEEK | RTP |
| megol® DP2718/55P0M | API SpA | SEBS | megol® |
| Formolene FORMAX® L91507E2 | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene FORMAX® |
| Laprene® 83E200A30 | SO.F.TER. SPA | SEBS | Laprene® |
| Hostacom HBC 308L W92607 | LyondellBasell Industries | PP Homopolymer | Hostacom |