DESLON™ 66 DSC201G9
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLON™ 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f4DOgc_DESLON-66-DSC201G9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLON™ DSC201G9 is one of the brands which made by Polyamide66 that filled Glass Fiber 45% and reinforced goods. It provides high mechanical strength, good fluidity property and excellent injection molding property. Applications: DESLON™ DSC201G9 is one of the most-used for high mechanical property and thermal property goods, such as Motor Fan of Mechanical and Automotive parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.60 | % | |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 206 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 12300 | MPa | ASTM D790 |
| Flexural Strength | 304 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 255 | °C | ASTM D648 |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 | |
| Arc Resistance | 110 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 285 | °C | |
| Front Temperature | 285 - 290 | °C | |
| Nozzle Temperature | 280 - 285 | °C | |
| Processing (Melt) Temp | 280 - 285 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® WR-12157 XRD | Teknor Apex Company | TPE | Monprene® |
| Generic TPO - Talc | Generic | TPO | Generic |
| Elastron® G P.G100.A70.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Hifax TYC 1123X | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| SQUARE® LIM3600-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |