HIVOREX 5200B
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HIVOREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f3IZWc_HIVOREX-5200B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIVOREX 5200B is produced by slurry process technology. This resin is ideally suited for use in blow molding application. HIVOREX 5200B is designed to offer high stiffness, excellent impact resistance, good resistance at low temp and chemicals resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.963 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | 30.0 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 28.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1470 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 540 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPE5305B | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| INEOS Wire & Cable BPD2142 | INEOS Olefins & Polymers Europe | LDPE | INEOS Wire & Cable |
| PLANAC BT-2230-27 | TOYOBO America, Inc. | PBT | PLANAC |
| AXLENE® 35RM | INDELPRO, S.A. de C.V. | PP Random Copolymer | AXLENE® |
| 3M™ Dyneon™ Fluoroelastomer FC 2179 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |