Latamid 12 G/50
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f2z2HX_Latamid-12-G-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 12 (PA 12). Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.75 to 1.0 | % | |
| Flow : 2.00 mm | 0.35 to 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 10500 | MPa | |
| 60°C | 6300 | MPa | |
| 90°C | 5100 | MPa | |
| 120°C | 4300 | MPa | |
| 150°C | 3300 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 150 | MPa | |
| Break, 60°C | 110 | MPa | |
| Break, 90°C | 90.0 | MPa | |
| Break, 120°C | 80.0 | MPa | |
| Break, 150°C | 55.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 6.0 | % | |
| Break, 23°C | 4.5 | % | |
| Break, 60°C | 6.0 | % | |
| Break, 90°C | 7.0 | % | |
| Break, 120°C | 8.0 | % | |
| Break, 150°C | 9.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 220 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 190 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | °C | |
| Vicat Softening Temperature | 180 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AR76WT6390 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| TOTAL Polypropylene Lumicene® M 3382 MZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| New-prene™ 9345N | Total Polymer Vision (Suzhou) Co., LTD | SEBS | New-prene™ |
| KOPLA PA66 KDE1020 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| LNP™ VERTON™ RX89047 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |