Hanwha Total PP TH54K
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f2VFDG_Hanwha-Total-PP-TH54K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TH54K is a super-heat-resistant polypropylene compound that exhibits significantly improved strength and heat-resistance due to the addition of the inorganic filler, talc to mo-polypropylene. This product employs a variety of base PPs, such as HIPP (High Isotactic or High crystalline Polypropylene), and are manufactured with HANWHA TOTAL's special processing technology to ensure quality. Superior rigidity, long-term heat resistance, anti-static property, and dimensional stability are characteristic of these products. super-heat-resistant PP compound is widely used in electric and electronic products that are subject to high temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 0.70 to 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 36.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 3 | 4120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 147 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 39.2 to 88.3 | MPa | |
| Holding Pressure | 58.8 to 98.1 | MPa | |
| Screw Speed | 30 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® PP HGZ-350SP | Saudi Polymers Company | PP Homopolymer | Marlex® PP |
| Thermoset Plastics 261 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| NEXUS PS 625 | Nexus Resin Group, LLC. | PS (HIPS) | NEXUS PS |
| ESTOPLAST EP 2030NN21 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| OTECH TPE OTE7030 - A/V Jacket | OTECH Corporation | TPE | OTECH TPE |