LG PS 460AF
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f0FnR0_LG-PS-460AF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG PS 460AF is a High Impact Polystyrene material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LG PS 460AF are:
Typical application of LG PS 460AF: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 93 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 23.0 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 3.20 mm | > 5.0 | % | |
| Break, 3.20 mm | 60 | % | |
| Flexural Modulus 3(3.20 mm) | 2160 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 37.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 39 | J/m | |
| -30°C, 6.40 mm | 39 | J/m | |
| 23°C, 3.20 mm | 88 | J/m | |
| 23°C, 6.40 mm | 69 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 84.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 78.0 | °C | |
| Vicat Softening Temperature | 84.0 | °C | ASTM D1525 5 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 70.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 200 to 210 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Varcum 29306 | Durez Corporation | Phenolic | Varcum |
| NEFTEKHIM PP 7300D | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Aurora PVC AP3040 Series | Aurora Plastics, Inc. | PVC, Rigid | Aurora PVC |
| Geon™ Vinyl Flexible XV3821 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Rotuba CAB B9004 (5% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |