VENYL UT400
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f01zgx_VENYL-UT400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UT400 is a 40% mineral filled polyamide 66 intended for Injection moulding. APPLICATIONS VENYL UT400 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties, this product offers reduced shrinkage, increased dimensional stability. VENYL UT400 is available in both black standard (VENYL UT400 - 8229) and natural (VENYL UT400) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.49 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 to 1.0 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.4 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| L-Scale | 100 | 82 | ||
| M-Scale | 80 | 53 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7500 | 5000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 80.0 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 5500 | 4000 | MPa | ISO 178 |
| Flexural Stress | 135 | 105 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | 7.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 25 | 35 | kJ/m² | ISO 179 |
| Notched Izod Impact | 50 | 70 | J/m | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 212 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 285 to 300 | °C | |
| Middle Temperature | 280 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 265 to 280 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-447 | Teknor Apex Company | TPE | Medalist® |
| SILVER® ABS 3360E | Guangdong Silver Age Sci & Tech. Co., Ltd | ABS | SILVER® |
| Zetpol® 2020 | Zeon Corporation | NBR | Zetpol® |
| LNP™ THERMOCOMP™ JF002 compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |
| Piolen® P T20A37 | PiO Kunststoffe GmbH & Co KG | PP Copolymer | Piolen® P |