Neopor® F 4 speed

Category:	PS (EPS) , Expanded Polystyrene
Manufacturer:	BASF Corporation
Trademark:	Neopor®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ezg20O_Neopor-F-4-speed.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Neopor® is used to manufacture silver-gray colored foams that have considerably better thermal insulation capacity than conventional EPS products. For the production of expanded foames having the fire characteristics in conformity with: DIN 4102-B1 (flame retardant) EN 13501-1-E For additional information pertaining to the fire behavior please contact the local BASF representative. Product description Expandable polystyrene (EPS) containing uniformly distributed flame-retardant. Blowing agent: pentane. Neopor® F 4 speed: For the production of blocks and shaps with wall thickness over 6 mm at densities ~25 kg/m 3 with low water up-take and short cylce time.

Message

Neopor® is used to manufacture silver-gray colored foams that have considerably better thermal insulation capacity than conventional EPS products.

For the production of expanded foames having the fire characteristics in conformity with:

DIN 4102-B1 (flame retardant)

EN 13501-1-E

For additional information pertaining to the fire behavior please contact the local BASF representative.

Product description
Expandable polystyrene (EPS) containing uniformly distributed flame-retardant. Blowing agent: pentane.

Neopor® F 4 speed: For the production of blocks and shaps with wall thickness over 6 mm at densities ~25 kg/m 3 with low water up-take and short cylce time.

General Information
Additive	Blowing Agent 2 Flame Retardant
Features	Flame Retardant
Uses	Foam Insulation
Agency Ratings	DIN 4102/B1 EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Appearance	Grey
Forms	Spheres

Physical	Nominal Value	Unit
Apparent Density
-- ¹	0.02	g/cm³
--	0.02 to 0.03	g/cm³
Moisture Content	< 3.5	%
Sieve Analysis
< 400.0 µm	< 2.0	%
400.0 to 1000.0 µm	> 96	%
> 1.00 mm	< 2.0	%

Additional Information	Nominal Value	Unit
Aging - intermediate	0.4 to 2.0	day
Bead Size	500.0 to 800.0	µm

Note Message
1 .	Obtainable in a single pre-foaming operation

Resin Grade	Manufacturer	Category	Trademark
ADDILENE H 520 M40	ADDIPLAST	PP Homopolymer	ADDILENE
Diaterm® A27 SR GF50	DTR S.r.l. (Develop Thermoplastic Resins)	Nylon 6	Diaterm®
Dryflex® WS 35M200	ELASTO	TPE	Dryflex®
LNP™ LUBRICOMP™ RFN16 compound	SABIC Innovative Plastics	Nylon 6	LNP™ LUBRICOMP™
Paxon™ HYA021L	ExxonMobil Chemical	HDPE, UHMW	Paxon™