Generic PPA - Glass Fiber
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ezeKos_Generic-PPA---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPA - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.32 - 1.72 | g/cm³ | ASTM D792 |
| 23°C | 1.29 - 1.78 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.19 - 0.51 | % | ASTM D955 |
| Transverse flow : 23°C | 0.47 - 1.0 | % | ASTM D955 |
| 23°C | 0.14 - 1.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.12 - 0.30 | % | ASTM D570 |
| 23°C, 24 hr | 0.30 - 0.51 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.21 - 1.2 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 5140 - 18600 | MPa | ASTM D638 |
| 23°C | 5200 - 18300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 68.9 - 250 | MPa | ASTM D638 |
| Yield, 23°C | 12.6 - 270 | MPa | ISO 527-2 |
| Fracture, 23°C | 163 - 199 | MPa | ASTM D638 |
| Fracture, 23°C | 109 - 263 | MPa | ISO 527-2 |
| 23°C | 88.5 - 260 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.5 - 2.6 | % | ASTM D638 |
| Yield, 23°C | 1.4 - 2.5 | % | ISO 527-2 |
| Fracture, 23°C | 1.0 - 2.5 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 3.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 5340 - 17600 | MPa | ASTM D790 |
| 23°C | 8820 - 14500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 126 - 364 | MPa | ASTM D790 |
| 23°C | 138 - 392 | MPa | ISO 178 |
| Yield, 23°C | 103 - 363 | MPa | ASTM D790 |
| Fracture, 23°C | 132 - 400 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 143 - 196 | MPa | ASTM D695 |
| Shear Strength (23°C) | 88.4 - 108 | MPa | ASTM D732 |
| Poisson's Ratio (23°C) | 0.41 | ASTM E132 | |
| Coefficient of Friction | 0.15 - 0.52 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.8 - 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 19 - 90 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 23 - 120 | J/m | ASTM D256 |
| 23°C | 2.5 - 14 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 190 - 1000 | J/m | ASTM D256 |
| 23°C | 20 - 71 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 1.76 - 10.1 | J | ASTM D3763 |
| 23°C | 1.44 - 3.74 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 276 - 308 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 273 - 313 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 297 - 320 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 247 - 292 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 250 - 305 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 284 - 300 | °C | ASTM D648 |
| 8.0 MPa, not annealed | 165 - 231 | °C | ISO 75-2/C |
| Continuous Use Temperature | 140 - 187 | °C | ASTM D794 |
| Vicat Softening Temperature | 259 - 314 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 300 - 315 | °C | ISO 11357-3 |
| -- | 310 - 313 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | |||
| Flow | 2.7E-6 - 3.6E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.3E-5 - 2.5E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.4E-5 - 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.5E-6 - 1.3E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 4.9E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 140 - 150 | °C | UL 746 |
| RTI Imp | 118 - 150 | °C | UL 746 |
| RTI | 119 - 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+2 - 2.5E+15 | ohms | ASTM D257 |
| -- | 1.0E+5 - 2.5E+16 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+3 - 2.5E+15 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 - 2.6E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 18 - 23 | kV/mm | ASTM D149 |
| 23°C | 17 - 42 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.66 - 5.52 | ASTM D150 | |
| 23°C | 3.66 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 4.0E-3 - 0.017 | ASTM D150 | |
| 23°C | 4.9E-3 - 0.015 | IEC 60250 | |
| Comparative Tracking Index (CTI) | 548 - 600 | V | UL 746 |
| Comparative Tracking Index | 593 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 746 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 720 - 928 | °C | IEC 60695-2-13 |
| Oxygen Index | 23 - 25 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 - 135 | °C | |
| Drying Time | 3.0 - 7.2 | hr | |
| Dew Point | -31.7 - -28.9 | °C | |
| Suggested Max Moisture | 0.045 - 0.15 | % | |
| Hopper Temperature | 70.0 - 79.4 | °C | |
| Rear Temperature | 310 - 326 | °C | |
| Middle Temperature | 321 - 330 | °C | |
| Front Temperature | 322 - 333 | °C | |
| Nozzle Temperature | 324 - 333 | °C | |
| Processing (Melt) Temp | 314 - 338 | °C | |
| Mold Temperature | 114 - 160 | °C | |
| Injection Pressure | 86.0 - 104 | MPa | |
| Back Pressure | 0.243 - 0.314 | MPa | |
| Screw Speed | 45 - 50 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPA - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 705A | RTP Company | LDPE | RTP |
| RTP 103 CC HI HB | RTP Company | PP, Unspecified | RTP |
| CERTENE™ PRB-2C | Muehlstein | PP Random Copolymer | CERTENE™ |
| LNP™ LUBRICOMP™ JX91198 compound | SABIC Innovative Plastics | PESU | LNP™ LUBRICOMP™ |
| Lupox® HI2100M | LG Chem Ltd. | PBT | Lupox® |