Nivionplast® A R306G NATURALE
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Nivionplast® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eyBaWV_Nivionplast-A-R306G-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber reinforced, heat stabilized polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 0.40 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 5.5 | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | % | |
| Ash Content | 30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 180 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 8500 | MPa | ASTM D790 |
| Flexural Strength | 270 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 95 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 250 | °C | |
| 1.8 MPa, Unannealed | 245 | °C | |
| Peak Melting Temperature | 260 | °C | ASTM D3417 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 285 | °C | |
| Front Temperature | 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 1640 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| ASI POLYPROPYLENE 1692 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Formolene® 3355E | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |
| KYOCERA KE-300K | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| TARFLON™ DK3722 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |