Category: | LCP , Liquid Crystal Polymer |
Manufacturer: | Mando Advanced Materials Co., Ltd. |
Trademark: | SEPAZ™ |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | ey2FAN_SEPAZ-C400TC.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
SEPAZ™ C400TC is a Liquid Crystal Polymer (LCP) product. It is available in Asia Pacific. Characteristics include:
|
General Information | |
---|---|
Features |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 2.69 | g/cm³ | ASTM D792 |
Molding Shrinkage - Flow 1 | 0.40 | % | ASTM D955 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength | 61.8 | MPa | ASTM D638 |
Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
Flexural Modulus | 12800 | MPa | ASTM D790 |
Flexural Strength | 90.2 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact | 32 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 243 | °C | ASTM D648 |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Volume Resistivity | 1.0E+12 | ohms·cm | ASTM D257 |
Flammability | Nominal Value | Unit | Test Method |
---|---|---|---|
Flame Rating | V-0 | UL 94 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Processing (Melt) Temp | 332 to 366 | °C | |
Mold Temperature | 66.0 to 121 | °C |
Note Message | |
---|---|
1 . | 60°C Mold Temperature |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
TRANSMARE® 10HT20-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
Clariant Nylon 6/6 PA-133G13 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
Laril 13 G/10-V1 | LATI S.p.A. | PPE+PS | Laril |
Karina IVORY PVC COMPOUND 90850-35/1-AY-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
Kepex® 4345GF | Korea Engineering Plastics Co., Ltd | PBT | Kepex® |