WELLAMID Nylon 6000 CFGV 15/15 HWCP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | CP-Polymer-Technik GmbH & Co. KG |
| Trademark: | WELLAMID Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ewyPDz_WELLAMID-Nylon-6000-CFGV-15-15-HWCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA6, 15 % carbon fibre reinforced, 15 % glass fibre reinforced, improved electrical conductivity, heat stabilized, virgin base polymer |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.31 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 2.00 mm | 0.80 | -- | % | |
| Flow : 2.00 mm | 0.30 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 to 2.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16000 | 12500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 175 | 125 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | 4.5 | % | ISO 527-2/5 |
| Flexural Modulus | 14000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 17 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | 75 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50 |
| Melting Temperature | 212 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+5 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+5 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ALC-55D | Biomerics, LLC | TPU-PC | Quadrathane™ |
| Sylvin 6214-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TEREZ PA 6.6 7500 GF 30 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Braskem PP RP 270G | Braskem | PP Random Copolymer | Braskem PP |
| Hax™ HFX 500 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |