LNP™ VERTON™ RX10409D compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ewwDCS_LNP-VERTON-RX10409D-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON RX10409D is a compound based on Nylon 66 containing proprietary fillers. Added feature of this grade is: Structural. Also known as: LNP* VERTON* Compound RX10409D Product reorder name: RX10409D |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 | % | |
| Across Flow : 24 hr | 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.66 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12000 | MPa | ASTM D638 |
| -- | 11800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 203 | MPa | ASTM D638 |
| Break | 199 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.4 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 11100 | MPa | ASTM D790 |
| -- 5 | 10300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 285 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 305 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 302 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 22 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength (23°C) | 88 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D256 |
| 23°C 8 | 24 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 9 | 76 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 22.0 | J | ASTM D3763 |
| -- | 7.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 258 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 258 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 253 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 253 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V857 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TPC PVC SM61E | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Ultraform® N 2640 Z4 | BASF Corporation | Acetal (POM) Copolymer+PUR | Ultraform® |
| Multilon® DN-3710F | TEIJIN LIMITED | PC+ABS | Multilon® |
| Axiall PVC 12805 | Axiall Corporation | PVC, Flexible | Axiall PVC |