MAJORIS BG364
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ewG8Nm_MAJORIS-BG364.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BG364 is a 30% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding and extrusion profiles. The product is available in natural, but other colours can be provided on request. BG364 has been developed especially for demanding applications in various engineering sectors. BG364 has high rigidity and good impact strength, good dimensional stability and good creep resistancy also at high temperatures. APPLICATIONS Product requiring very high overall mechanical performance such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.60 - 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.3 | % | ISO 527-2/50 |
| Flexural Modulus | 4500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 16 | kJ/m² | ISO 180/1A |
| 23°C | 21 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 148 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 132 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A |
| -- | 122 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 30.0 - 70.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBIT® VS1503 | Samyang Corporation | PBT | TRIBIT® |
| ELASTOSIL® M 4511 | Wacker Chemie AG | Silicone | ELASTOSIL® M |
| HIPTEN® 21015 | HIP-PetroHemija | LDPE | HIPTEN® |
| Sylvin 9067-85 Yellow 4127 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ BFL4000U resin | SABIC Innovative Plastics | PC | LEXAN™ |