SABIC® HDPE ICP5505
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ew4PM9_SABIC-HDPE-ICP5505.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE ICP5505 is part of SABIC's new breakthrough high density polyethylene Industial Container Product portfolio. The grade meets latest market expectations regarding property balance and processing behaviour. SABIC® HDPE ICP5505 is typically used for state of the art blow moulding UN approved Open Head drums, from 25 up to 220 liter and more. This food approved grade is also very suited for the production of UN approved Jerry Cans. It combines excellent rigidity and impact with optimal stress crack resistance and easy processing performance, which offers potential system cost reduction. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.955 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 5.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C, Molded) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1100 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 23°C, 2.00mm, molded | 26.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 23°C, 2.00mm, molded | 40.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1300 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 27.0 | MPa | ISO 178 |
| ESCR (Strain Hardening) - Gp | 17.0 | MPa | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Enthalpy Change | 207 | J/g | ISO 11357-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-30°C, Compression Molded) | 34 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 82.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 128 | °C | ISO 306/A |
| Melting Temperature (DSC) | 133 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ML-1130B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| Vistalon™ 8731 | ExxonMobil Chemical | EPDM | Vistalon™ |
| Celazole® (U-Series) U-60ESD | PBI Performance Products, Inc. | PBI | Celazole® (U-Series) |
| DURACON® TF-10LV | Polyplastics Co., Ltd. | Acetal (POM) Copolymer+PUR | DURACON® |
| HI-ZEX™ 232J | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |