LNP™ LUBRICOMP™ JFL36 compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eusLpT_LNPLUBRICOMPJFL36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP JFL36 is a compound based on Polyethersulfone resin containing Glass Fiber, PTFE. Also known as: LNP* LUBRICOMP* Compound JFL-4036 Product reorder name: JFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.69 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.15 - 0.35 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 117 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 7700 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.46 | ASTM D3702 Modified | |
| With Self-Static | 0.36 | ASTM D3702 Modified | |
| Wear Factor - Washer | 60.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 223 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 219 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 4.9E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 360 - 371 | °C | |
| Front Temperature | 371 - 382 | °C | |
| Processing (Melt) Temp | 354 - 371 | °C | |
| Mold Temperature | 138 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PC A 1000/100 | ALBIS PLASTIC GmbH | PC | ALTECH® PC |
| Elastollan® 1185A10V-Film | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Braskem PE LDF2023S1 | Braskem IDESA | LDPE | Braskem PE |
| Sinvicomp SZS7068A-E5A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | SINVICOMP |
| ESTOPLAST XU 4201GY01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |