TECHNYL® A 50H1 BLACK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eug3ET_TECHNYLA50H1BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 50H1 Black is an unreinforced Non-phosphorous and Non-halogenated flame retardant polyamide 66, heat stabilized, for injection moulding. This flame retardant grade, offers excellent filling qualities combined with good stiffness. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183/A |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.88 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.7 | -- | % | ISO 62 |
| Outdoor Suitability | f1 | -- | UL 746C |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3800 | 1700 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield, 23°C | 80.0 | 50.0 | MPa | ISO 527-2/1A |
| Fracture, 23°C | 75.0 | 40.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break, 23°C) | 9.0 | > 100 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 3800 | 1750 | MPa | ASTM D790 |
| 23°C | 3700 | 1700 | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 120 | 50.0 | MPa | ASTM D790 |
| 23°C | 130 | 55.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 3.2 | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 80 kJ/m² | No Break | ISO 179/1eU | |
| Notched Izod Impact | ||||
| 23°C | 40 | -- | J/m | ASTM D256 |
| 23°C | 3.0 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 237 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 85.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 3.0E+15 | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | |||
| 0.800 mm | 33 | -- | kV/mm | IEC 60243-1 |
| 2.00 mm | 21 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.50 | -- | IEC 60250 | |
| Dissipation Factor | 0.017 | -- | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.40 mm | V-0 | -- | UL 94 | |
| 0.8 mm | V-0 | -- | UL 94 | |
| 1.6 mm | V-0 | -- | UL 94 | |
| 3.2 mm | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.8 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.6 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.2 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.40 mm | 960 | -- | °C | IEC 60695-2-13 |
| 0.8 mm | 960 | -- | °C | IEC 60695-2-13 |
| 1.6 mm | 775 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 33 | -- | % | ISO 4589-2 |
| French Fire Index | F2 | -- | NF F16-101 | |
| French Smoke Index | I2 | -- | NF F16-101 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| European Railways Certifications | EN 45545-2 | |||
| R22 | HL3 | -- | EN 45545-2 | |
| R23 | HL3 | -- | EN 45545-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 265 - 275 | °C | |
| Front Temperature | 265 - 275 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: All reinforced flame retardant compounds generate some level of abrasion/corrosion to the steel processing equipment. These issues can be worsened by using incorrect processing conditions (temperatures, residence time, moisture level ...) during the moulding process. Therefore, Solvay recommends to use the advised processing conditions detailed in this technical data sheet. For equipment that comes into contact with molten flame retarded compounds, Solvay advises to use a steel containing high chromium & high carbon content (minimum concentration of 16% Chromium) to prevent corrosion and abrasion. For the correct reference of steel associated to flame retardant compounds processing, please refer to your equipment manufacturers. For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature at 120°C. Of course it should be noted that this improvement in the surface appearance may be at the expense of the cycle time. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BorECO™ BC212IM | Borealis AG | PP Copolymer | BorECO™ |
| Globalene® TPV 1065A BK | Lee Chang Yung Chemical Industry Corp. | TPV | Globalene® |
| Hifax TRC 221X | LyondellBasell Industries | PP Copolymer | Hifax |
| Jackdaw PP ER14BK8003 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |
| Geon™ Vinyl Flexible HC18580 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |