Hostacom G3 U01 L
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | euRTyK_Hostacom-G3-U01-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
"Hostacom" G3 U01 L is a 30% glass fiber reinforced PP homopolymer (coupled) The product is designed for injection molding of washing machine parts and is available in natural color It is not intended for medical, pharmaceutical or drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 15 | g/10 min | |
| 230°C/5.0 kg | 55 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 230°C/2.16 kg | 15.0 | cm³/10min | |
| 230°C/5.0 kg | 58.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 120 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 6800 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 95.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus - Secant (23°C) | 5600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 125 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -20°C | 7.5 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1 |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 35 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ISO 306/A50 |
| -- | 165 | °C | ISO 306/B50 |
| RTI Elec | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Str | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm, ALL | HB | ||
| 1.50 mm, ALL | HB | ||
| 3.00 mm, ALL | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT GP2101 | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Vipel® F010-TBN-28 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| ELASTOSIL® P 7950 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® P |
| PENTAMID B S GVB16 H2 black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| ULTEM™ DH1004 resin | SABIC Innovative Plastics | PEI | ULTEM™ |