LNP™ LUBRICOMP™ KP003AXZ compound
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eu6Gfw_LNP-LUBRICOMP-KP003AXZ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KP003AXZ is a compound based on Acetal Homopolymer resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KL-4530 D Product reorder name: KP003AXZ |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 2.4 | % | |
| Across Flow : 24 hr | 2.5 | % | |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2570 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 53.1 | MPa | ASTM D638 |
| Yield | 53.0 | MPa | ISO 527-2 |
| Break | 52.4 | MPa | ASTM D638 |
| Break | 53.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 21 | % | ASTM D638 |
| Yield | 15 | % | ISO 527-2 |
| Break | 29 | % | ASTM D638 |
| Break | 15 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.21 | ||
| vs. Itself - Static | 0.11 | ||
| Wear Factor - Washer | 11.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 5.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 3 | 53 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 1.10 | J | ASTM D3763 |
| -- | 1.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 162 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 157 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 92.8 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 88.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 9.6E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 9.6E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanguang TPU Y-95AX | Fujian Nanguang Light Industry Co., Ltd. | TPU, Unspecified | Nanguang TPU |
| Nycast Nyloil-FG | Cast Nylons Ltd. | Nylon 6 | Nycast |
| Borealis PP ZP961 | Borealis AG | TPO | Borealis PP |
| K-vinyl 70 Deg C Rating Sheathing (Dry) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| SABIC® PPcompound 55T1030 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |