Eastar™ DN003, Natural
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Eastar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ethDYg_Eastar-DN003-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eastar™ Copolyester DN003 has been tested for FDA/ISO 10993 and USP Class VI Biological Evaluation testing after Gamma and EtO sterilization. Eastar™ Copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. DN003 contains a mold release. This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®. The GREENGUARD INDOOR AIR QUALITY CERTIFIED® Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.23 | g/cm³ | ASTM D792 |
| 23°C | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.13 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 45.0 | MPa | ASTM D638 |
| Yield, 23°C, 4.00 mm | 46.0 | MPa | ISO 527-2 |
| Break, 23°C | 52.0 | MPa | ASTM D638 |
| Break, 23°C, 4.00 mm | 47.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 5.0 | % | ASTM D638 |
| Yield, 23°C, 4.00 mm | 4.4 | % | ISO 527-2 |
| Break, 23°C | 330 | % | ASTM D638 |
| Break, 23°C, 4.00 mm | 230 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1800 | MPa | ASTM D790 |
| 23°C, 4.00 mm | 1800 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C, 4.00 mm | 63.0 | MPa | ISO 178 |
| Yield, 23°C | 66.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 64 | J/m | ASTM D256 |
| 23°C | No Break | ASTM D256 | |
| -40°C | 7.4 | kJ/m² | ISO 180 |
| 23°C | 130 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D4218 | ||
| -40°C | No Break | ||
| 23°C | No Break | ||
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -40°C, Energy to Peak Force | 16.0 | J | |
| 23°C, Energy to Peak Force | 14.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 74.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 64.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 88.0 | °C | ASTM D1525, ISO 306/A 2 1 |
| -- | 79.0 | °C | ISO 306/B |
| Specific Heat | DSC | ||
| 60°C | 1340 | J/kg/°C | |
| 240°C | 2050 | J/kg/°C | |
| Thermal Conductivity (23°C) | 0.19 | W/m/K |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.0 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 15.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN HE-362M | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| POLYLAN AG12A0 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| AKROMID® A3 GF 50 natural (2423) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Fiberfil® J-60/40/E8 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| ADENE® O07HFB-D01 | A.D. Compound S.p.A. | PP Homopolymer | ADENE® |