Marlex® HMN 55180
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Polymers Company |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | et42Fs_Marlex-HMN-55180.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
This hexene copolymer is tailored for injection moulding applications that require:
Typical injection moulded applications for HMN 55180 include items such as:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded, F50) | < 20.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 29.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 140 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : Molding | 1290 | MPa | ASTM D790 |
| Tangent : Molding | 1350 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, unannealed, molded | 75.0 | °C | ASTM D648A |
| 1.8 MPa, unannealed, molded | 50.0 | °C | ASTM D648A |
| Brittleness Temperature 3 | < -75.0 | °C | ASTM D746A |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 4 |
| Additional Information |
|---|
| The physical properties were determined on compression moulded specimens that were prepared in accordance with Procedure C of ASTM D4703, Annex A1. |
| Note Message | |
|---|---|
| 1 . | Type 4, 51mm/min |
| 2 . | Type 4, 51mm/min |
| 3 . | Type I specimen |
| 4 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P25M | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Royalex Royalex | Spartech Plastics | ABS+PVC | Royalex |
| Nylene® NX4301 | Custom Resins Group | Nylon 6 | Nylene® |
| Hostaform® M10AE | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| OnFlex™ V 3050D-S0097 | PolyOne Corporation | TPE | OnFlex™ |