Geon™ Vinyl Flexible A5501
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Flexible |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | esspSD_Geon-Vinyl-Flexible-A5501.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Specialty flexible molding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 43 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Break | 6.62 | MPa | |
| 100% Strain | 2.74 | MPa | |
| Tensile Elongation 2(Break) | 320 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 3 | 29.2 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -46.5 | °C | ASTM D746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 138 to 149 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 132 to 143 | °C |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | Die C, 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 282E TFE 13 SI 2 | RTP Company | Nylon, Unspecified | RTP |
| PROTEQ™ C24UST2 | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| Softell CA 02 A | LyondellBasell Industries | Polyolefin, Unspecified | Softell |
| ACCUTECH™ CP0437G5M25CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Daelim Po1y® PP-164 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |