Hanwha Total PE 532L
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eseyRY_Hanwha-Total-PE-532L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 532L is a low-density polyethylene resin for skin layer of multi-layer lamination films. This grade is designed to be processed in conventional blown film equipment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.8 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 12.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Apparent Bending Modulus | 275 | MPa | ASTM D747 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 40 µm | 22.6 | MPa | ASTM D882 |
| TD : Yield, 40 µm | 15.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm | 240 | % | ASTM D882 |
| TD : Break, 40 µm | 590 | % | ASTM D882 |
| Dart Drop Impact (40 µm) | 65 | g | ASTM D1709 |
| Seal Initiation Temperature (40 µm) | 140 | °C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 1 |
| Melting Temperature | 113 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm) | 75 | ASTM D2457 | |
| Haze (40.0 µm) | 6.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Heat Seal Strength, SAMSUNG TOTAL: 1200 g/cm²Fish-eye, SAMSUNG TOTAL: 1 ea/g |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 130 - 150 | °C | |
| Cylinder Zone 2 Temp. | 130 - 150 | °C | |
| Cylinder Zone 3 Temp. | 130 - 150 | °C | |
| Cylinder Zone 4 Temp. | 130 - 150 | °C | |
| Cylinder Zone 5 Temp. | 130 - 150 | °C | |
| Melt Temperature | 160 | °C | |
| Die Temperature | 160 - 170 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 1 to 2 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLON 2500 G2 | Taro Plast S.p.A. | PC | TAROLON |
| Vinnolit® P 70 PS | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| ExxonMobil™ LLDPE LL 8460 Series | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Hifax BR1149AC | LyondellBasell Industries | TPO (POE) | Hifax |
| Sylvin 9067-60 Grey 9174 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |