Hax™ HFX 509/1
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Fainplast Compounds S.r.l |
| Trademark: | Hax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | esMZop_Hax-HFX-509-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GRAFTED HALOGEN FREE, FLAME RETARDANT AND LOW SMOKE EMISSION COMPOUND, CURABLE BY EXPOSURE TO MOISTURE FOR SOLAR CABLE INSULATION This product is a LSFOH silane grafted compound for cable insulation, Cross-linkable by heat and moisture by previous addition of a suitable catalyst masterbatch (SIOPLAS method). It is highly recommended to store separately the grafted compound and the catalyst, as prescorching may take place during the reactive extrusion. The properties of this compound meet the requirements of EN 50363-0 type G9 & G10,CEI 20-91type G21. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Wire Types |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (150°C/21.6 kg) | 5.0 | g/10 min | ISO 1133 |
| Water Absorption - 24 hrs (100°C) 1 | 1.50 | mg/cm² | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Set 2 | IEC 60811 | ||
| Elongation under load : 200°C | 20 | % | |
| Elongation under load : 250°C | 30 | % | |
| Permanent elongation after cooling : 200°C | 0.0 | % | |
| Permanent elongation after cooling : 250°C | 5.0 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gas Evolved Acidity - HCl & HBr | < 0.50 | % | EN 50267-2-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 160 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 48 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Break 3 | 12.5 | MPa | IEC 60811 |
| Break | 11.5 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Break 4 | 250 | % | IEC 60811 |
| Break | 290 | % | ISO 527-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 20°C 5 | 2.0E+15 | ohms·cm | |
| 20°C | 5.0E+15 | ohms·cm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 30 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 130 | °C | |
| Cylinder Zone 2 Temp. | 140 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 155 | °C | |
| Adapter Temperature | 155 | °C | |
| Die Temperature | 165 | °C |
| Note Message | |
|---|---|
| 1 . | After Crosslinking |
| 2 . | 15mins, 0.2 N/mm², After Crosslinking |
| 3 . | After Crosslinking |
| 4 . | After Crosslinking |
| 5 . | After Crosslinking |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ 34-1520 SSM TFPP | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Daplen™ EE108AE | Borealis AG | TPO | Daplen™ |
| Ferro PP LPP20BN34HB | Ferro Corporation | PP, Unspecified | Ferro PP |
| HANWHA LDPE 5310 | Hanwha Chemical | LDPE | HANWHA LDPE |
| Hy-Vin® XN78036 | INEOS Compounds | PVC, Flexible | Hy-Vin® |