TRIBOCOMP® POM AF10 TS0
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | erqw1K_TRIBOCOMP-POM-AF10-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® POM AF10 TS0 is an Acetal (POM) Copolymer product filled with 10% aramid fiber and 10% ptfe fiber. It is available in Europe. Primary characteristic: copolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.8 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 65.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| vs. Itself - Dynamic | 0.11 | ||
| vs. Itself - Static | 0.070 | ||
| Wear Factor | 11 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 135 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 8.0E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.23 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 to 210 | °C | |
| Cylinder Zone 2 Temp. | 170 to 220 | °C | |
| Cylinder Zone 3 Temp. | 180 to 220 | °C | |
| Cylinder Zone 4 Temp. | 200 to 225 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom POM-C 2A/2L1 | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| Zetpol® 2001 | Zeon Chemicals L.P. | NBR | Zetpol® |
| Fainplast PVC PH 60/AS | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| INSTRUC PPSLGFMIN65 | Infinity LTL Engineered Compounds | PPS | INSTRUC |
| LNP™ STAT-KON™ ME003S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |