Bergadur™ BR3300-8022 RS BK001
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergadur™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | erEpxM_Bergadur-BR3300-8022-RS-BK001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass fiber reinforced PBT compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 115 | MPa | ASTM D638 |
| Flexural Modulus 2 | 6000 | MPa | ASTM D790 |
| Flexural Strength 3 | 185 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 195 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Charge Decay Time - 12% RH, 5000 kV to 50 kV | 277777774164.2 | hr | MIL B-81705C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 240 - 270 | °C | |
| Middle Temperature | 240 - 270 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Mold Temperature | 75.0 - 95.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Regis® E6541 | Noble Polymers | Polyolefin, Unspecified | Regis® |
| TEKAMID™ TA210L | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Utomer UT10P80A | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| HyTemp® AR12 | Zeon Chemicals L.P. | Acrylic, Unspecified | HyTemp® |
| Sylvin 86042-75 Clear 8422 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |