Durethan® DP AKV 50 HR H2.0 901510
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | er0GDT_DurethanDPAKV50HRH20901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 50 % glass fibers, injection molding, heat-aging stabilized, hydrolysis stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.57 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 300°C, 2.00mm 1 | 0.92 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.11 | -- | % | ISO 294-4 |
| Flow direction : 300°C, 2.00mm 3 | 0.37 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.050 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 15500 | 10600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 220 | 159 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.7 | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 15500 | 10500 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% strain | -- | 237 | MPa | ISO 178/A |
| 23°C | 355 | 260 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 3.1 | 4.6 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GHRW, 14-160, GF50 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 15 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 110 | 100 | kJ/m² | ISO 179/1eU |
| 23°C | 100 | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 13 | 14 | kJ/m² | ISO 180/1A |
| 23°C | 15 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 90 | 85 | kJ/m² | ISO 180/1U |
| 23°C | 90 | 85 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | -- | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex VE-0852 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Syncure™ System S112FH | PolyOne Corporation | XLPE | Syncure™ |
| Badaflex® TPE-S 40A 1462 AB transparent | Bada AG | SEBS | Badaflex® |
| LTP PA6125 | Chengdu Letian Plastics Co., Ltd | TP, Unspecified | LTP |
| LNP™ THERMOCOMP™ JF003E compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |