LNP™ LUBRICOMP™ WFL34 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eqbeCg_LNP-LUBRICOMP-WFL34-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* WFL34 is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound WFL-4034 Product reorder name: WFL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.054 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.072 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 7890 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 118 | MPa | ASTM D638 |
| Yield | 114 | MPa | ISO 527-2/5 |
| Break 3 | 118 | MPa | ASTM D638 |
| Break | 114 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.6 | % | ASTM D638 |
| Yield | 2.6 | % | ISO 527-2/5 |
| Break 5 | 2.6 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 7480 | MPa | ASTM D790 |
| -- 7 | 7070 | MPa | ISO 178 |
| Flexural Strength 8 | ASTM D790 | ||
| Yield, 50.0 mm Span | 173 | MPa | |
| Break, 50.0 mm Span | 173 | MPa | |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.24 | ||
| vs. Itself - Static | 0.22 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | -0.0200 to -0.0100 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 44.5 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 9 | 7.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 680 | J/m | ASTM D4812 |
| 23°C 10 | 41 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.50 | J | ASTM D3763 |
| -- | 2.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 222 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 222 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 210 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 208 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 HS | RTP Company | Nylon 66 | RTP |
| Sinvicomp SIM4009 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Network Polymers LDPE 10 2523 | Network Polymers, Inc. | LDPE | Network Polymers LDPE |
| Next Nylon 66 Prime Series PGHSLR30-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Bergamid™ A70 GK30 black 13539126 | PolyOne Corporation | Nylon 66 | Bergamid™ |