Hostalen GF 9045 F
| Category: | HDPE, MMW , High Density (MMW) Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eqAHM6_Hostalen-GF-9045-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen GF 9045F is a high density Polyethylene, having medium molar mass and a narrow molecular mass distribution. Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.946 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 21 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 1.8 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 21.0 | MPa | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Film Thickness - Recommended / Available | 0.8-3.1 mil (20-80 µ) | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 30 µm, blown film | 45.0 | MPa | ISO 527-3 |
| TD : 30 µm, blown film | 28.0 | MPa | ISO 527-3 |
| Tensile Elongation - MD (Broken, 30 µm, blown film) | 520 | % | ISO 527-3 |
| Dart Drop Impact (30 µm, Blown Film) | 45 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 73.0 | °C | ISO 306/B50 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Staudinger Index | 260 | cm³/g | ISO 1628 |
| Film properties tested using 30 µm thickness blown film extruded at a melt temperature of 190°C and a blow-up ratio of 3:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Semitron® ESd 225 | Quadrant Engineering Plastic Products | Acetal (POM) Homopolymer | Quadrant EPP |
| Teflon® PTFE 7A X | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| Bapolene® 5010H | Bamberger Polymers, Inc. | HDPE, HMW | Bapolene® |
| Evermore PUR UP-9320N | Evermore Chemical Industry Co., Ltd. | PUR-Ether | Evermore PUR |
| Jamplast PET EX-03 | Jamplast, Inc. | PET | Jamplast |