OnFlex™ S KA 40A-3S1767
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | OnFlex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eptcqp_OnFlex-S-KA-40A-3S1767.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OnFlex™-S KA thermoplastic elastomer polymer is mixed with hydrogenated styrene block copolymer. This series of polymers has good compatibility and can provide excellent adhesion to polyamide polymer materials, such as PA6, PA6.6, PA11 and PA12. OnFlex-S KA polymer can be processed by 2K molding or multiple injection molding, plug-in molding or co-extrusion. In addition, OnFlex™-S KA polymer has good compression set even at high temperatures, its processability is good, the hardness range is large, the bending at low temperatures, scratch resistance, coloring, surface appearance, mechanical properties, etc. are good, and excellent UV resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | Internal method | ||
| Vertical flow direction : 72 hours, 2.00mm | 0.90 | % | Internal method |
| Flow direction : 72 hours, 2.00mm | 2.9 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 40 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% strain | 1.00 | MPa | ISO 37 |
| 300% strain | 2.30 | MPa | ISO 37 |
| Tensile Stress (Break) | 3.00 | MPa | ISO 37 |
| Tensile Elongation (Break) | 410 | % | ISO 37 |
| Tear Strength | 17 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 13 | % | ISO 815 |
| 70°C, 22 hr | 29 | % | ISO 815 |
| 100°C, 22 hr | 57 | % | ISO 815 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| General Material Type | Styrene thermoplastic elastomers (TES) | ||
| 各项属性值是采用注射模制基板测量得出。 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 200 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | The results may vary according to process parameters, part geometry, and tool design when measuring 100x100x2mm of the substrate. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PBT T324 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| Nypol® PA B3 G50 HS UV PRTA010 NT304 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| FHR Polypropylene P9H2M-061X | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Latilub 73/13-15T G/15 | LATI S.p.A. | Acetal (POM) Copolymer | Latilub |
| Dynalloy™ GP 7810-30T | PolyOne Corporation | TPE | Dynalloy™ |