DOMAMID® 6ST1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics SPA |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | epgmig_DOMAMID-6ST1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, improved impact resistance, for injection moulding. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 2577 | |||
| Across Flow : 23°C, 72 hr | 1.4 to 1.6 | -- | % | |
| Flow : 23°C, 72 hr | 1.1 to 1.3 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.6 | -- | % | |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2700 | 1000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 70.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 50 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2300 | 900 | MPa | ISO 178 |
| Flexural Stress 3 | 90.0 | 30.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | 80 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength (23°C) | 15 | 75 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | No Break | No Break | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 155 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 190 | -- | °C | ISO 306/B50 |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene HDPE 50100.2 | TOTAL Refining & Chemicals | HDPE, HMW | TOTAL Polyethylene |
| HONES® PA66 G25 | Guangdong Shunde Hones Polymer Material Co., Ltd. | Nylon 66 | HONES® |
| IROGRAN® CA116-201 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Deprene 151-90 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |
| SD POLYCA™ 875G20F | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |