SABIC® LDPE 2404AF00
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | epD8Es_SABIC-LDPE-2404AF00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC®LDPE 2404AF00 is a low density polyethylene product,. It can be processed by extrusion coating and is available in Europe. SABIC®The application areas of LDPE 2404AF00 include food contact applications and coating applications. The main characteristics are: strong adhesion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.2 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance 1(60°C, 2.00mm, molded) | 3.00 | hr | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/200 | ||
| Yield, 1.60mm, molded | 11.0 | MPa | ISO 527-2/200 |
| Fracture, 1.60mm, molded | 14.0 | MPa | ISO 527-2/200 |
| Tensile Strain (fracture, 1.60mm, molded) | 640 | % | ISO 527-2/200 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm | 10.0 | MPa | ISO 527-3 |
| TD : Yield, 25 µm | 9.00 | MPa | ISO 527-3 |
| MD : 25 µm | 14.0 | MPa | ISO 527-3 |
| TD : 25 µm | 13.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 300 | % | ISO 527-3 |
| TD : Break, 25 µm | 450 | % | ISO 527-3 |
| Water Vapor Transmission Rate (38°C, 100% RH, 25 µm) | 18 | g/m²/24 hr | Internal method |
| Oxygen Permeability (23°C, 25.0 µm) 2 | 0.80 | cm³/cm²/bar/24 hr | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Enthalpy Change | 124 | J/g | DIN 53765 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Crack Resistance (25.0 µm) | 2400 | cycles/10 holes | Internal method |
| Tear Strength | ISO 6383-2 | ||
| MD : 25.0 µm | 12.0 | kN/m | ISO 6383-2 |
| TD : 25.0 µm | 9.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306 |
| Melting Temperature (DSC) | 111 | °C | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | 2 MPa |
| 2 . | 0% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Westlake LDPE EF923 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| HAIPLEN H50 Y0 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| ESTACARB 1560 V0 | Cossa Polimeri S.r.l. | PC | ESTACARB |
| OnForce™ LFT NN-30LGF/000 HS SP UV BLACK | PolyOne Corporation | Nylon 66 | OnForce™ LFT |
| KMI PP KMA450-K6R9P | KMI Group, Inc. | PP Random Copolymer | KMI PP |