EMERGE™ PC 8600-10
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eoNxhx_EMERGE-PC-8600-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 8600 is translucent, ignition-resistant polycarbonate resin. This resin contains no bromine, chlorine or phosphate additives and is intended to comply with global environmental standards. It is an easy flow PC resin suitable for use in injection molded applications in the computer, electronics, electrical, and information technology equipment markets. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, 3.20 mm, Injection Molded | 123 | ASTM D785 | |
| R-Scale, 4.00 mm | 123 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20 mm, Injection Molded | 2210 | MPa | ASTM D638 |
| 4.00 mm, Injection Molded | 2200 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield, 3.20 mm, Injection Molded 1 | 60.0 | MPa | ASTM D638 |
| Yield, 4.00 mm, Injection Molded | 60.0 | MPa | ISO 527-2/50 |
| Break, 3.20 mm, Injection Molded | 57.9 | MPa | ASTM D638 |
| Break, 4.00 mm, Injection Molded | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield, 3.20 mm, Injection Molded | 6.2 | % | ASTM D638 |
| Yield, 4.00 mm, Injection Molded | 6.0 | % | ISO 527-2/50 |
| Break, 3.20 mm, Injection Molded | 110 | % | ASTM D638 |
| Break, 4.00 mm, Injection Molded | 110 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 3.20 mm, Injection Molded | 2400 | MPa | ASTM D790 |
| 4.00 mm, Injection Molded 2 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| 3.20 mm, Injection Molded | 93.8 | MPa | ASTM D790 |
| 4.00 mm, Injection Molded 3 | 94.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.20 mm, Injection Molded | 750 | J/m | ASTM D256 |
| 23°C, Injection Molded 4 | 10 | kJ/m² | ISO 180/A |
| Instrumented Dart Impact (23°C, 3.20 mm, Total Energy) | 58.8 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 139 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 127 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ASTM D1525 5 |
| -- | 150 | °C | ISO 306/A120 |
| -- | 144 | °C | ISO 306/B50 |
| Ball Indentation Temperature | > 125 | °C | IEC 60335-1 |
| CLTE - Flow (-22 to 85°C) | 6.5E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 6(1.59 mm) | V-0 | Internal Method | |
| Glow Wire Ignition Temperature 7(2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index 8 | 35 | % | ASTM D2863, ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 271 to 288 | °C | |
| Mold Temperature | 65.6 to 98.9 | °C |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 4 mm |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| 6 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 7 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 8 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 805 TFE 5 | RTP Company | Acetal (POM) Copolymer | RTP |
| CarmelStat™ CS 5118 | Carmel Olefins Ltd. | PP, Unspecified | CarmelStat™ |
| Kingfa AP-201 | Kingfa | PP, Unspecified | Kingfa |
| Sylvin 8250-70 Brown 7461 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL GTX™ GTX979 resin | SABIC Innovative Plastics Europe | PPE+PS+Nylon | NORYL GTX™ |