Telcar® TL-2895E X (PRELIMINARY DATA)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eoEpv1_TelcarTL2895EXPRELIMINARYDATA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Telcar®TL-2895E X (PRELIMINARY DATA) is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Telcar®The main features of TL-2895E X (PRELIMINARY DATA) are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.878 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 1 sec | 85 | ASTM D2240 | |
| Shaw A, 5 seconds | 80 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| Transverse flow : 100% strain | 4.08 | MPa | ASTM D412 |
| Flow : 100% strain | 5.81 | MPa | ASTM D412 |
| Transverse flow : 300% strain | 5.19 | MPa | ASTM D412 |
| Flow : 300% strain | 7.19 | MPa | ASTM D412 |
| Tensile Strength 2 | ASTM D412 | ||
| Transverse flow : Fracture | 18.1 | MPa | ASTM D412 |
| Flow : Fracture | 10.1 | MPa | ASTM D412 |
| Tensile Elongation 3 | ASTM D412 | ||
| Transverse flow : Fracture | 810 | % | ASTM D412 |
| Flow : Fracture | 580 | % | ASTM D412 |
| Tear Strength 4 | ASTM D624 | ||
| Transverse flow | 58.7 | kN/m | ASTM D624 |
| Flow | 55.5 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 23°C, 22 hr | 23 | % | ASTM D395B |
| 70°C, 22 hr | 79 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 216 | °C | |
| Middle Temperature | 213 - 221 | °C | |
| Front Temperature | 221 - 227 | °C | |
| Nozzle Temperature | 221 - 229 | °C | |
| Processing (Melt) Temp | 221 - 229 | °C | |
| Mold Temperature | 25 - 66 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 210 | °C | |
| Cylinder Zone 2 Temp. | 199 - 216 | °C | |
| Cylinder Zone 3 Temp. | 213 - 221 | °C | |
| Cylinder Zone 5 Temp. | 221 - 227 | °C | |
| Die Temperature | 221 - 229 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | C mold, 510mm/min |
| 2 . | C mold, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WEVO-CHEMIE Polyurethanes PU 9251 FL/300 RE | WEVO-CHEMIE GmbH | PUR, Unspecified | WEVO-CHEMIE Polyurethanes |
| NYCOA Polyamide 567 | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| APEX® 1017 | Teknor Apex Company | PVC, Semi-Rigid | APEX® |
| LNP™ THERMOCOMP™ Lexan_JK500 compound | SABIC Innovative Plastics | PC+ABS | LNP™ THERMOCOMP™ |
| OnForce™ LFT LF0100-5001 NATURAL | PolyOne Corporation | PUR, Unspecified | OnForce™ LFT |