Toyolac® 100G-30
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | envY2q_Toyolac-100G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toyolac® 100G-30 is an Acrylonitrile Butadiene Styrene (ABS) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.26 | g/cm³ | ASTM D792 |
| 23°C | 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.10 to 0.30 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 125 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 118 | MPa | ASTM D638 |
| 23°C | 109 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break, 23°C | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8500 | MPa | ASTM D790 |
| 23°C | 8950 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 160 | MPa | ASTM D790 |
| 23°C | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C, 12.7 mm) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 104 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Catalyst CT/2 | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| Ferro PP LPP40BD25GY | Ferro Corporation | PP Homopolymer | Ferro PP |
| Hostacom G2 N02 100000 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Mafill® CT 4102 | Ravago Group | PP Copolymer | Mafill® |
| LNP™ THERMOCOMP™ AF002 compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |