LNP™ THERMOCOMP™ EX06430H compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | emTSYW_LNP-THERMOCOMP-EX06430H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP EX06430H is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this grade is: Healthcare. Also known as: LNP* THERMOCOMP* Compound EX06430H Product reorder name: EX06430H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 to 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 | % | |
| Across Flow : 24 hr | 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3660 | MPa | ASTM D638 |
| -- | 3500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 110 | MPa | ASTM D638 |
| Yield | 106 | MPa | ISO 527-2 |
| Break | 90.3 | MPa | ASTM D638 |
| Break | 90.6 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.7 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2 |
| Break | 14 | % | ASTM D638 |
| Break | 11 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3670 | MPa | ASTM D790 |
| -- | 3500 | MPa | ISO 178 |
| Flexural Stress | 133 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1400 | J/m | ASTM D4812 |
| 23°C 3 | 74 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 10.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 196 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 195 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN SRX-373 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| VITAMIDE® AI12WT6430 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| UMG ABS® LM-A | UMG ABS, Ltd. | ABS | UMG ABS® |
| Dion COR-RES 6693FR | Reichhold Chemicals, Inc. | Polyester, TS | Dion |
| DOMAMID® 6G15H | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |