Polylink Polymer Pipe PP 410/401
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Polylink Polymers (India) Ltd. |
| Trademark: | Polylink Polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | emBMfi_Polylink-Polymer-Pipe-PP-410-401.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This Compound utilizes the ststem for cross linking fo polyethylene developed by DOW corning and kown as Sioplan It is a two component comprising a silyated Ethylene Polymer Known as the graft copolymer PP 410 and a master batch PP 401 contaning a cross linking catalyst. The two materials are normally used in the ratio fo 95 parts graft to 5 parts catalyst master batch |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 22.0 | MPa | IEC 60811 |
| Tensile Strain 2(Break) | 400 | % | IEC 60811 |
| Flexural Modulus | 1200 | MPa | ASTM D790 |
| Flexural Strength | 27.5 | MPa | ASTM D790 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | 10 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (135°C, 168 hr) | -15 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset | IEC 60811 | ||
| Elongation underload | 85 | % | IEC 60811 |
| Permanent elongation after cooling | 5.0 | % | IEC 60811 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 140 | °C | |
| Cylinder Zone 2 Temp. | 175 | °C | |
| Cylinder Zone 3 Temp. | 185 | °C | |
| Cylinder Zone 4 Temp. | 195 | °C | |
| Cylinder Zone 5 Temp. | 205 | °C |
| Extrusion instructions |
|---|
| Zone 6 : 210°C-235°CScrew water temperature : 60 to70°CScreens : 30,50, 100(mesh apertures per linear inch)L/D Ratio: 20Compression: 2.5:1 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® M60075 | Reliance Industries Limited | HDPE | RELENE® |
| Sylvin 9708-80C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nipol® NBR DN212 | Zeon Corporation | NBR | Nipol® NBR |
| Kinta FR2600 | Kinta Technology (Hong Kong) Co., Ltd. | PP, Unspecified | Kinta |
| Sylvin 8299-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |