Ultramid® A3K FC Aqua UN

Category:	Nylon 66 , Polyamide 66
Manufacturer:	BASF Corporation
Trademark:	Ultramid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	elwvLf_Ultramid-A3K-FC-Aqua-UN.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Ultramid® A3K FC Aqua UN is optimized for plastic parts, mandatory requiring material approvals for drinking water or direct food contact.

General Information
Features	Compliance of Food Exposure
Uses	Non-specific food applications Potable water application
Agency Ratings	ACS not rated DVGW W270 EC 1907/2006 (REACH) EC 2023/2006 FDA 21 CFR 177.1500 KTW not rated NSF Not Rated WRAS not rated Europe 10/1/2011 12:00:00 AM
RoHS Compliance	RoHS compliance
Forms	Particle
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.13	--	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)	115	--	cm³/10min	ISO 1133
Water Absorption				ISO 62
Saturated, 23°C	8.0 - 9.0	--	%	ISO 62
Equilibrium, 23°C, 50% RH	2.5 - 3.1	--	%	ISO 62
Viscosity Number (96% H2SO4)	150	--	cm³/g	ISO 307
Mold Shrinkage - constrained ¹	0.85	--	%

Thermal	Dry	Conditioned	Unit	Test Method
Temperature index- at 50% loss of tensile strength				IEC 60216
-- ²	118	--	°C	IEC 60216
-- ³	101	--	°C	IEC 60216
Maximum operating temperature- short cycle operation	200	--	°C

Additional Information	Dry	Conditioned		Test Method
Automotive Materials (> 1.00 mm)	Pass	--		FMVSS 302

Injection	Dry	Unit
Screw Speed		mm/sec

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	3100	1100	MPa	ISO 527-2
Tensile Stress (Yield)	85.0	50.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	5.0	20	%	ISO 527-2/50
Nominal Tensile Strain at Break	30	> 50	%	ISO 527-2/50
Tensile Creep Modulus ⁴(1000 hr)	--	700	MPa	ISO 899-1
Flexural Modulus	2900	--	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	4.0	--	kJ/m²	ISO 179/1eA
23°C	5.0	20	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break	No Break		ISO 179/1eU
Notched Izod Impact				ISO 180/A
-30°C	6.0	--	kJ/m²	ISO 180/A
23°C	5.5 kJ/m²	No Break		ISO 180/A

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	220	--	°C	ISO 75-2/B
1.8 MPa, not annealed	75.0	--	°C	ISO 75-2/A
Melting Temperature	260	--	°C	ISO 11357-3
CLTE - Flow (23 to 80°C)	7.0E-5 - 1.0E-4	--	cm/cm/°C	ISO 11359-2
Specific Heat	1700	--	J/kg/°C
Thermal Conductivity	0.33	--	W/m/K	DIN 52612

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	--	1.0E+10	ohms	IEC 60093
Volume Resistivity	1.0E+15	1.0E+12	ohms·cm	IEC 60093
Relative Permittivity (1 MHz)	3.20	5.00		IEC 60250
Dissipation Factor (1 MHz)	0.025	0.20		IEC 60250
Comparative Tracking Index (Solution A)	600	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (1.60 mm)	V-2	--		UL 94

Injection	Dry	Unit
Drying Temperature	80.0	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.15	%
Hopper Temperature	80.0	°C
Rear Temperature	290	°C
Middle Temperature	290	°C
Front Temperature	290	°C
Nozzle Temperature	290	°C
Processing (Melt) Temp	280 - 300	°C
Mold Temperature	60.0 - 80.0	°C

Injection instructions
Residence Time: <10 min.

Note Message
1 .	Test box with central gating, dimensions of base (107471,5) mm, processing condition: TM = 290°C, TW = 60°C
2 .	5000 h
3 .	20000 h
4 .	strain <= 0.5%, 23°C

Resin Grade	Manufacturer	Category	Trademark
Ming Dih EPS S	Ming Dih Group Corporation	PS (EPS)	Ming Dih EPS
SITRALIN 21E / C6PS soul	SITRAPLAS GmbH	ASA+Nylon	SITRALIN
Hostacom X M2 U43	LyondellBasell Industries	PP Copolymer	Hostacom
Hylon® N2000HL	Ravago Manufacturing Americas, LLC	Nylon 6	Hylon®
PLUSTEK RA303G6	Polyram Ram-On Industries	Nylon 66	PLUSTEK