Starflam PZ0052E
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starflam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | elt3Br_Starflam-PZ0052E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PZ0052E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced Polyamide 6 Molding Resin (known as PF1005Z222 or PA625GFUZ22) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.39 | g/cm³ | ASTM D792 |
| -- | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 0.40 to 0.60 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 1.1 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7440 | MPa | ASTM D638 |
| -- | 6100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 103 | MPa | ASTM D638 |
| Break | 82.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.3 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7100 | MPa | ASTM D790 |
| -- | 5200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 144 | MPa | ASTM D790 |
| -- | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 470 | J/m | ASTM D4812 |
| 23°C 3 | 25 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.00 | J | ASTM D3763 |
| -- | 8.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 215 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 204 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 137 | °C | ISO 75-2/Af |
| CLTE - Flow (-40 to 40°C) | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm, Tested by E2P) | V-2 | UL 94 | |
| Oxygen Index | > 20 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ISPLEN® PP 099 K2M | REPSOL | PP Homopolymer | ISPLEN® |
| LNP™ STAT-KON™ PD000 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ STAT-KON™ |
| MAJORIS FW300 - 1335 | AD majoris | PP, Unspecified | MAJORIS |
| SQUARE® LSG6931-20A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| LNP™ THERMOCOMP™ EF006H compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |