TITANLENE® LDC 801YY
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Lotte Chemical Titan (M) Sdn. Bhd. |
| Trademark: | TITANLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | elLay5_TITANLENE-LDC-801YY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDC801YY is a low density polyethylene resin for extrusion coating and is a barefoot grade. LDC801YY meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 2.1 & (c) 2.2. APPLICATIONS: Coating for all substrates. Characteristics: Excellent drawdown, good heat seability and adhesion properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | 230000 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (25 µm, 38°C, 90% RH) | 19 | g·mm/m²/atm/24 hr | ASTM F372 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 86.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 270 to 340 | °C | |
| Neck-in 1(295°C) | 90.0 | mm |
| Note Message | |
|---|---|
| 1 . | constant output 50 m/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® N 2320 U03 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| BMC 840-7271 | Bulk Molding Compounds, Inc. | Vinyl Ester | BMC |
| LIHAN® A706 | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| Pier One ABS L3-BK09 | Pier One Polymers, Inc. | ABS | Pier One ABS |
| PLUSTEK PB305G33 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |