Order Products : sales@su-jiao.com
TUFLIN™ HSE-7002 NT 7
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | TUFLIN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ekzzRs_TUFLIN-HSE-7002-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
TUFLIN™ HSE-7002 NT 7 Linear Low Density Polyethylene Resin is an ethylene-hexene-1 copolymer designed for cast stretch film applications such as industrial pallet wrap. Films containing HSE-7002 offer outstanding puncture, toughness and load holding properties. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Energy | Internal method | ||
| 20 µm | 4.29 | J | Internal method |
| 51 µm | 8.81 | J | Internal method |
| Film Puncture Force | Internal method | ||
| 20 µm | 44.5 | N | Internal method |
| 51 µm | 89.0 | N | Internal method |
| Film Puncture Resistance | Internal method | ||
| 20 µm | 30.8 | J/cm³ | Internal method |
| 51 µm | 24.0 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 20 µm | 203 | J/cm³ | ASTM D882 |
| MD : 51 µm | 225 | J/cm³ | ASTM D882 |
| TD : 20 µm | 358 | J/cm³ | ASTM D882 |
| TD : 51 µm | 262 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 20 µm | 142 | MPa | ASTM D882 |
| 2% secant, MD : 51 µm | 138 | MPa | ASTM D882 |
| 2% secant, TD : 20 µm | 150 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 138 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 10.6 | MPa | ASTM D882 |
| MD : Yield, 51 µm | 9.82 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 11.3 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 10.3 | MPa | ASTM D882 |
| MD : Break, 20 µm | 55.7 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 38.4 | MPa | ASTM D882 |
| TD : Break, 20 µm | 47.2 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 37.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 480 | % | ASTM D882 |
| MD : Fracture, 51 µm | 700 | % | ASTM D882 |
| TD : Break, 20 µm | 890 | % | ASTM D882 |
| TD : Fracture, 51 µm | 800 | % | ASTM D882 |
| Dart Drop Impact | |||
| 20 µm | 130 | g | ASTM D1709A |
| 20 µm | < 100 | g | ASTM D1709B |
| 51 µm | 330 | g | ASTM D1709A |
| 51 µm | 210 | g | ASTM D1709B |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 20 µm | 220 | g | ASTM D1922 |
| MD : 51 µm | 790 | g | ASTM D1922 |
| TD : 20 µm | 640 | g | ASTM D1922 |
| TD : 51 µm | 1100 | g | ASTM D1922 |
| Unstretched bond | ASTM D5458 | ||
| 20.3 µm | 220 | g | ASTM D5458 |
| 50.8 µm | 310 | g | ASTM D5458 |
| Final stretch 2 | Internal method | ||
| 20.3 µm | 300 | % | Internal method |
| 50.8 µm | 470 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20°, 20.3 µm | 157 | ASTM D2457 | |
| 20°, 50.8 µm | 149 | ASTM D2457 | |
| 45°, 20.3 µm | 95 | ASTM D2457 | |
| 45°, 50.8 µm | 91 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 20.3 µm | 1.0 | % | ASTM D1003 |
| 50.8 µm | 3.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 274 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： EGAN/Davis 标准 5 层铸造生产线 熔体温度：525 °F (274 °C) 冷却辊（主/次）温度：70 °F (21 °C) 生产线速度：0.8 密尔 = 600 fpm（183 米/分）；2.0 密尔 = 200 fpm（61 米/分） 输出：0.8 密尔 = 401 磅/小时；2.0 密尔 = 340 磅/小时 模具宽度：36 英寸 (914 mm) 模具间隙：25 密尔 (0.65 mm) 气隙：3 英寸 (76 mm) |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Testing on pallets; highlighting Industries Inc. test methods. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7500 GF 25 FLB/2 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| New-prene™ 8380N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| APEX® 1563 | Teknor Apex Company | PVC, Flexible | APEX® |
| Etinox® EI-6530 | Ercros, S.A. | PVC, Flexible | Etinox® |
| POLYFLAM® SDR 5005 WHITE 88315 HP25 | A. Schulman Europe | PS (GPPS) | POLYFLAM® |